SF-1B Bronze Base Bearing for Heavy Machinery and Equipment

SF-1B bronze basic bearing is made of tin bronze as the base, sintered bronze spherical powder in the middle, and rolled PTFE and high temperature resistant filling materials on the surface. It has a high safety factor and is particularly suitable for places where continuous operation cannot be stopped for repairs and places where high temperature cannot be refueled. It has been widely used in the metallurgical steel industry, continuous casting machine billet raceways, high temperature furnace front equipment, cement grouting pumps and screw conveyors. It can be combined with steel sleeves on the outside, or it can be made into flanges to achieve the effect of simultaneous friction of the end face and the inner hole. The sliding part of the bridge support uses SF-1B wear-resistant layer thickened products to replace pure PTFE plates to meet the requirements of 130N/mm2 shaft load.

إقتبس

PREV：SF-1D Hydraulic Special Bearing High-Performance for Hydraulic Systems NEXT：SF-1W Durable Self-Lubricating Lead-Free Bearing Corrosion-Resistant

مقدمة المنتج
معامل
وصف المادة
اتصل بنا

مواصفات المنتج

1 يمكن أن تعمل لفترة طويلة في ظل ظروف خالية من الزيت.

2 أكثر ملاءمة لظروف العمل ذات السرعة المنخفضة والأحمال الثقيلة، مع مقاومة جيدة للتآكل و احتكاك منخفض للغاية.

3 مناسبة للحالات التي يصعب فيها تشكيل طبقة زيتية، مثل الترددية والدورية و حركات متقطعة.

4 مقاومة للتآكل والأكسدة.

5 صيانة مجانية وعمر خدمة طويل.

لماذا تختار المحامل بدون زيت

تقليل تكاليف التصنيع

ليست هناك حاجة لجهاز إمداد الزيت أو فتحة حقن الزيت أو الزيت معالجة الأخدود، والتي يمكن أن توفر تكاليف التصنيع بشكل كبير.

تقليل تكاليف التشغيل

إنه يقلل بشكل كبير من استخدام زيت التشحيم، ويقلل من صيانة المعدات، ويتجنب المخاطر الخفية الناجمة عن عدم كفاية إمدادات النفط، مما يقلل بشكل فعال تكاليف التشغيل.

تقصير وقت التصميم

يعمل التصميم الخالي من الزيت على تبسيط هيكل المنتج وتوفير وقت التصميم بشكل فعال. نحن محترفون موردي ODM SF-1B Bronze Base Bearing for Heavy Machinery and Equipment

يفضي إلى حماية البيئة

ليست هناك حاجة لإعادة تدوير نفايات الزيوت، وهو أمر مفيد أيضًا لحماية البيئة.

مجالات التطبيق

درجة حرارة عالية

·مصنع الصلب

· فرن الصهر

· معدات التجفيف

·فرن الخبز

· جهاز التحكم بالحرارة

ضد للماء

· بوابة السد

· مضخة مياه

· هيكل تبديل السوائل

· الهياكل البحرية

· معدات آلة الرصيف والطمي

الصناعة الكيميائية

· مصنع كيماويات

· معدات الطلاء الكهربائي

· معدات معالجة مياه الصرف الصحي

· آلات الصباغة

· معدات تكرير النفط والكيماويات

طاقة

·قوة الرياح

·طاقة جديدة

سفينة

· رافعة سطح السفينة

·مِرسَاة

· غطاء الفتحة

· ذراع الدفة

· آلات الرفع ومعدات حلقة الرفع

تصنيع السيارات

· ختم القالب

· هيكل اللحام

· خط الطلاء والتجفيف

· الحزام الناقل المعدني

·أدوات الآلة

الصناعات الثقيلة

· ماكينات مصنع الأنابيب الفولاذية

· مصانع الإطارات والورق

·محطة توليد الكهرباء

· ربط تبديل آلات حقن القالب

البناء والتعدين والتحميل

· الخلاطات والمطاحن والساحقات

· آلات البناء

·ادوات المنجم

· توصيل محامل قضيب

الجسور وقضبان الرفع

· محامل الجسر

· الكمرات والجسور والجسور المعلقة

· المفاعلات المرتبطة بالطاقة النووية

·مولد البخار

Technical Parameters

●Maximum bearing pressure: 140N/mm2
●Applicable temperature range: -195~+300℃
●Maximum sliding speed: 5m/s
●Friction coefficient: 0.03~0.18
●Maximum allowable PV value (dry): 4.3N/mm2 .m/s
●Maximum allowable PV value (oil): 50N/mm2 .m/s

Metallographic Structure and Material Structure

①Polytetrafluoroethylene and lead mixture 0.01~0.03mm
②Spherical bronze powder 0.2~0.3mm
③Copper back 0.7~2.3mm

Application Features

●The mixture of PTFE and lead can form a good transfer film to protect the grinding shaft during movement.
●The sintered layer and the copper substrate have good thermal conductivity and can quickly transfer the heat generated during operation.
●Copper has self-lubricating properties and can be used in parts that cannot be shut down for maintenance due to long-term operation.
●The base copper has good corrosion resistance and can be used in weak acid and strong alkali situations.
●It has good load-bearing capacity.
●The product has been widely used in the metallurgical steel industry, high-temperature furnace steel ring parts, cement grouting pumps, screw conveyors, port machinery and ship machinery, etc.
●It can be combined with a steel sleeve on the outside; or made into a flange to achieve the effect of using the inner hole and the end face at the same time.

Chemical Properties

Model	Air	Vacuum	Water	Steam	Weak acid	Medium acid	Strong acid	Alkaline solution
SF-1B	good	good	good	good	medium	N/A	N/A	good

MMD-10 End Surface Friction and Wear Test

Model	Test Duration	Test Conditions			Friction Coefficient	Final Temperature	Final Wear Amount
Model	Test Duration	Lubrication Type	Speed	Pressure	Friction Coefficient	(℃)	(mm)
SF-1B	3hr	Dry	0.4m/s	3.5N/mm2	0.151	83	0.014
SF-1B	3hr	Oil	0.4m/s	3.5N/mm2	0.058	55	0.012

تكوين المواد وخصائصها
مادة	CuZn25Al5Mn3Fe3	CuSn5Pb5Zn5	CuAl10Ni5Fe5	CuSn12	CuZn25Al5Mn4Fe3
كثافة	8.0	8.9	7.8	8.9	8.0
صلابة HB	> 210	> 70	> 150	> 95	> 250
قوة الشد N/mm²	> 750	> 200	> 600	> 260	> 800
قوة الخضوع N/mm²	> 450	> 90	> 260	> 150	> 450
استطالة٪	>12	>15	>10	>ح	> 800
معامل التوسع الخطي 10 ^-5 / درجة مئوية	1.9	1.8	1.6	1.8	1.9
الحد من درجة الحرارة	-40~300	-40~400	-40~400	-40~400	-40~150
الأعلى. تحميل ن/مم²	100	60	50	70	120
الأعلى. السرعة (جاف) م/دقيقة	15	10	20	10	15
Max.PV N/mm²*m/min	200	60	60	80	200
ضغط التشوه الدائم 300 نيوتن/مم²	<0.01	<0.05	<0.04	<0.05	<0.05
* الطلب الكبير على المواد الخاصة متوفر.

تبادل المواد الأساسية
رموز المواد	العلامات التجارية الصينية GB1176-87	دولي ايزو 1338	ألمانيا الدين	اليابان جيس	أمريكا أستم (أونس)	إنكلترا بكالوريوس	إيطاليا جي إم	الشروط المطبقة
JDB مصبوب من البرونز	ZCuZn25AI5 Fe3Mn3	GCUZn25AI6 Fe3Mn3	DIN1709 G-CuZn25AI5	H5102 كاك304	ب30-92 C86300	HTB2	JM18-1	تحميل عالي، سرعة منخفضة شائعة الاستخدام
JDB-1برونزية	ZCuSn5 Pb5Zn5	GCUPb5 Sn5Zn5	DIN1705 G-CuSn5ZnPb	H5111 قبل الميلاد6	ب30-92 C83600	إل جي2	JM7-15	متوسط التحميل، وسرعة منخفضة شائعة الاستخدام
JDB-2برونزية	ZCuAI9Fe4 Ni4Mn2	GCUAI10 الحديد NiS	DIN17656 G-CuAI10Ni	H5114 ايبك3	ب30-92 C95500	AB2	JM3-15	متوسط التحميل، متوسط السرعة، شائع الاستخدام
JDB-3برونزية	ZCuSn12		G-CuSn12	CAC503B	ب30-92 C90800	PB2	JM1-15	تحميل متوسط، سرعة منخفضة، شائع الاستخدام
جي دي بي-5	ZCuZn25AI6 Fe3Mn3	GCUZn25AI6 Fe3Mn3	DIN1709 G-CuZn25AI5	H5102 كاك304	ب30-92 C86300	HTB2	JM18-1	يتم استخدام حمولة عالية وسرعة منخفضة وحمولة عالية

زيوت التشحيم الصلبة
المزلق	سمات	تطبيق نموذجي
SL1 إضافة الجرافيت	مقاومة ممتازة ضد المواد الكيميائية الهجمات والاحتكاك المنخفض، حد درجة الحرارة 400 درجة مئوية	دعوى للآلات العامة و تحت الغلاف الجوي
إس إل 4 إضافة PTFE	أقل احتكاك وجيد للتزييت المائي، حد درجة الحرارة 300 درجة مئوية	السفينة، التوربينات الهيدروليكية، توربينات الغاز، الخ

SUBMIT

معلومات عنا

Zhejiang Mingxu Machinery Manufacturing Co., Ltd. موردي ODM المعروف سابقًا باسم Jiashan Mingxu Precision Machinery Factory، تم تأسيسه في عام 2011. وتقع الشركة في المناطق النائية لمنطقة العرض التوضيحي للتنمية المتكاملة لدلتا نهر اليانغتسى، مع الموقع ووسائل النقل المريحة. مع أكثر من عشر سنوات من الخبرة في التصنيع والبحث والتطوير، شاركت الشركة بعمق في تطوير وإنتاج محامل التشحيم الصلبة، وألواح التزلج، والممرات المنزلقة، والمتزلجات. موردو ODM وشركة JFB لجلبة الكتف ذات شفة الجرافيت المطعمة ذاتية التشحيم في الصين. يعتمد تصنيع المنتج معدات التشغيل الآلي الحديثة، وينفذ بدقة معيار نظام إدارة الجودة ISO2000، وتتم معالجة العمليات الرئيسية بواسطة آلات CNC عالية الدقة. تغطي المنتجات الرئيسية للشركة سلسلة من المنتجات مثل محامل التشحيم الذاتي الصلبة المطعمة JDB، والمحامل الملبدة بالنحاس والصلب، ومحامل التشحيم الذاتي SF-1، ومحامل التشحيم الذاتي الحدودية SF-2، ومحامل النحاس FB090. تستخدم على نطاق واسع في صناعة السيارات، وآلات البناء، والمعدات المعدنية، وآلات التعدين، وقولبة الحقن، والعفن، والمنسوجات، والطباعة والعديد من مجالات تصنيع الآلات الأخرى؛ حتى الآن، انتشرت منتجات الشركة في جميع أنحاء الصين وتم تصديرها إلى العديد من البلدان الأجنبية، وهي معترف بها بشدة ومحبوبة من قبل العملاء المحليين والأجانب. تلتزم Mingxu Machinery بمبدأ الخدمة المتمثل في "الخدمة عالية الجودة الموجهة نحو الجودة"، وتسعى جاهدة لتزويد العملاء بالمنتجات والخدمات الاحترافية. توريد الجملة MXB-JFB الكتف جلبة شفة الجرافيت مطعمة تحمل التشحيم الذاتي. ستواصل الشركة تقديم المواهب وتحسين آلية الإدارة والنزاهة والتطوير والابتكار والسعي لبناء علامة تجارية عالمية المستوى.